| Chemical composition (weight %) (Maximum values unless range is shown) | |||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| O | N | C | H | Fe | Al | V | Ni | Mo | Others | Residuals | |
| 0.20 | 0.05 | 0.08 | 0.015 | 0.40 | 5.5–6.75 | 3.5–4.5 | 0.4 | ||||
Grade 2 is the most widely used titanium allow in all product forms for industrial service, offering an excellent balance of moderate strength and reasonable ductility. Highly corrosion-resistant in highly oxidizing and mildly reducing environments, including chlorides.
| Mechanical properties at room temperature | ||
|---|---|---|
| Minimum values | Typical values | |
| Yield Strength | 825 MPa | 910 MPa |
| Ultimate Strength | 895 MPa | 1000 MPa |
| Elongation in 50 mm, A5 | 10% | 18% |
| Reduction in Area | 20% | % |
| Hardness | 330–390 HV | |
| Modulus of elasticity | 114 GPa | |
| Charpy V-Notch Impact | 20–27 J | |