| Chemical composition (weight %) (Maximum values unless range is shown) | |||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| O | N | C | H | Fe | Al | V | Ni | Mo | Others | Residuals | |
| 0.18 | 0.03 | 0.08 | 0.015 | 0.2 | 0.4 | ||||||
Unalloyed titanium offering optimum ductility and cold formability with useful strength, high-impact toughness, and excellent weldability. Highly corrosion resistant in oxidizing and mildly reducing environments, including chlorides.
| Mechanical properties at room temperature | ||
|---|---|---|
| Minimum values | Typical values | |
| Yield Strength | 170 MPa | 220 MPa |
| Ultimate Strength | 240 MPa | 345 MPa |
| Elongation in 50 mm, A5 | 25% | 37% |
| Reduction in Area | 30% | 0% |
| Hardness | 115 HV | |
| Modulus of elasticity | 103 GPa | |
| Charpy V-Notch Impact | 95-162 J | |